Effects of Na/K ratio on the phase structure and electrical properties of Na_xK_(1-x)NbO_3 lead-free piezoelectric ceramics  

作　　者：ZHANG Qian, ZHANG Boping, Li Haitao, and SHANG Pengpeng School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China 

出　　处：《Rare Metals》2010年第2期220-225,共6页稀有金属（英文版）

基　　金：supported by the National Natural Science Foundation of China (No. 50842028);the National Basic Research Priorities Program of China (No. 2007CB613301)

摘　　要：Lead-free piezoelectric NaxK1-xNbO3（x = 0.3-0.8）（NKN） ceramics were fabricated by normal sintering at 1060°C for 2 h.Microstructures and electrical properties of the ceramics were investigated with a special emphasis on the influence of Na content.The grain size of the produced dense ceramic was decreased by increasing Na content.A discontinuous change in the space distance was found at the composition close to Na0.7K0.3NbO3 ceramic, which indicates the presence of a transitional composition between two different orthorhombic phases, which is similar to the behavior of morphotropic phase boundary（MPB） in NaxK1-xNbO3 ceramics.Such MPB-like behavior contributes to the enhanced piezoelectric coefficient d33 of 122 pC/N, planar-mode electromechanical coupling coefficient kP of 28.6%, and dielectric constant εr of 703, respectively for the Na0.7K0.3NbO3 ceramic.Cubic temperature TC and the transitional temperature TO-T from orthorhombic to tetragonal phase are observed at around 420°C and 200°C, respectively.Lead-free piezoelectric NaxK1-xNbO3（x = 0.3-0.8）（NKN） ceramics were fabricated by normal sintering at 1060°C for 2 h.Microstructures and electrical properties of the ceramics were investigated with a special emphasis on the influence of Na content.The grain size of the produced dense ceramic was decreased by increasing Na content.A discontinuous change in the space distance was found at the composition close to Na0.7K0.3NbO3 ceramic, which indicates the presence of a transitional composition between two different orthorhombic phases, which is similar to the behavior of morphotropic phase boundary（MPB） in NaxK1-xNbO3 ceramics.Such MPB-like behavior contributes to the enhanced piezoelectric coefficient d33 of 122 pC/N, planar-mode electromechanical coupling coefficient kP of 28.6%, and dielectric constant εr of 703, respectively for the Na0.7K0.3NbO3 ceramic.Cubic temperature TC and the transitional temperature TO-T from orthorhombic to tetragonal phase are observed at around 420°C and 200°C, respectively.

关 键 词：lead-free piezoelectric ceramics NKN sintering morphotropic phase boundary（MPB） 

分 类 号：TQ174.7[化学工程—陶瓷工业]