合成与表征新型介-微孔Y型分子筛Meso-NaY  

Synthesis and Characterization Meso-NaY- A New Meso-micro-porous Materials

作　　者：陈平娥[1,2] 刘洪涛[1] 

机构地区：[1]北京化工大学理学院现代催化研究所,北京100029 [2]山西大同大学化学与化工学院,山西大同037009

出　　处：《山西大同大学学报（自然科学版）》2010年第2期41-43,共3页Journal of Shanxi Datong University(Natural Science Edition)

基　　金：国家自然科学基金[20606003]

摘　　要：应用新型模板剂炭黑对Y型分子筛进行组装合成具有介孔孔道的Y型分子筛.通过XRD、FT-IR结果表明,炭黑的加入降低了Y型分子筛结晶度.通过BET表征材料具有介孔孔道(3.8 nm),Meso-NaY的总比表面积和孔容分别为736 m2/g和0.373 cm3/g.材料中介孔所占的比例很少,还不能达到长程有序,如何在Y型分子筛中引进长程有序的介孔材料将是今后研究的方向.Zeolite Y of mesoporous channels have been synthesized using novel mesoporous carbon black as template under alkaline conditions. The results of XRD, FT-IR showed that the crystalation of the materials decreased with the increasing of the carbon black ; The results of BET suggested that the composites had mesoporous structure （3.8 nm）. The proportion of mesoporous is very few, can not achieve long-range order. How can introduct the long-range ordered mesoporous materials into the Y-zeolite will be fu- ture research directions.

关 键 词：Y型分子筛 介-微孔Y型分子筛 炭黑硬模板剂 表征 

分 类 号：O643[理学—物理化学]