东烧厂提高烧结料层厚度的试验研究  

Experimental Study on Improvement Sintering Bed Height at East Anshan Sintering Plant of AISC

作　　者：王常秋[1] 侯恩俭[1] 吴铿[2] 何海熙[2] 尹晓莹[2] 杨森[2] 

机构地区：[1]鞍钢集团矿业公司东烧厂,辽宁鞍山114000 [2]北京科技大学冶金与生态工程学院,北京100083

出　　处：《钢铁》2010年第4期10-12,30,共4页Iron and Steel

基　　金：国家高技术研究发展(863)计划资助项目(2009AA0621487974);国家自然科学基金"钢铁联合研究基金"(50874129)

摘　　要：在实验室条件下,以鞍钢集团矿业公司东烧厂赤浮精矿为主要原料进行了600 mm提高到700 mm的厚料层烧结杯试验,获得了生产化学成分稳定、机械强度高、粒度均匀、高温冶金性能良好烧结矿的最佳生产工艺参数,给出了烧结过程中参数变化对烧结矿技术经济指标的影响规律,为鞍钢东烧厂进一步提高料层厚度提供了依据。The hematite concentrate was one of the main raw materials at East Anshan Sintering Plant.Under the laboratory conditions,sinter pot tests with bed height enhanced from 600mm to 700mm were carried out.The optimized process parameters,such as high stability of chemical compositions,high mechanical strength,uniform size distribution and good metallurgical qualities at high temperature,were obtained.The relationships between sintering parameters and technical-economic index were investigated.These results could provide the theoretical basis for further enhance ment of the sintering bed height.

关 键 词：赤浮精矿 厚料层 烧结杯试验 工艺参数 

分 类 号：TF046.4[冶金工程—冶金物理化学]