膨润土再生砂对 CO_2 水玻璃再生砂性能的影响  

Influence of the Reclaimed Bentonite Bonded Sand on the Reclaimed CO 2 Sodium Silicate Bonded Sand

作　　者：肖波[1] 徐正达[1] 王秀萍[1] REINHARD DOPP 

机构地区：[1]华中理工大学材料科学与工程学院 [2]德国克劳斯塔尔工业大学

出　　处：《华中理工大学学报》1998年第A01期31-33,共3页Journal of Huazhong University of Science and Technology

摘　　要：将膨润土湿型砂和ＣＯ２水玻璃砂分别进行机械法再生，再按不同比例混合，用ＣＯ２水玻璃工艺研究了再生砂的主要工艺性能．研究结果表明，膨润土再生砂对ＣＯ２水玻璃再生砂的影响不大，随着膨润土再生砂比例的增加，混合再生砂的终强度缓慢降低，而８００℃的残留强度急剧下降．Bentonite bonded sand and CO 2 Sodium silicate bonded sand were separately reclaimed mechanically, then the two kinds of reclaimed sand were mixed at different rates. Main technological properties of the mixture were studied with CO 2 curing process. It was shown that the initial strength and bench life of reclaimed sodium silicate bonded sand are little influenced by bentonite bonded sand. However, with increasing amount of bentonite bonded sand, the final strength of mixture is decreasing slowly and the retained strength at 800℃ is sharply declined.

关 键 词：CO2 水玻璃砂 膨润土砂 混合再生砂 型砂 

分 类 号：TG221.1[金属学及工艺—铸造]