挤压温度对退火态ZL102合金组织和性能的影响  

Effect of Extrusion Temperature on Microstructure and Mechanical Properties of ZL102 Aluminum Alloy in Annealing State

作　　者：曲明洋[1] 李保成[1] 张治民[2] 

机构地区：[1]中北大学材料科学与工程学院,山西太原030051 [2]山西省集成精密成形工程中心,山西太原030051

出　　处：《热加工工艺》2010年第7期38-40,共3页Hot Working Technology

基　　金：国家自然科学基金资助项目(50735005)

摘　　要：研究了退火态ZL102铸造铝合金在300～460℃和挤压比为15时的热变形对其组织和性能的影响。结果表明,退火后的铸态ZL102铝合金随着挤压温度的升高,硅颗粒先变小后变大,亚晶由小长大,强度先升高后降低,塑性变化不明显。在挤压温度为420℃时,材料强度最佳,抗拉强度达164MPa,屈服强度达53MPa,伸长率达21%。The influences of temperature（300～460 ℃） and extrusion ratio（15） on microstructure and properties of the annealing state of ZL102 aluminum alloy were studied.The results show that,with the extrusion temperature of as cast ZL102 aluminum alloy after annealing increasing,silicon particles in the alloy first become smaller and then become larger,subgrain grows up from small,the intensity first improves and then becomes lower,plasticity does＇t change significantly.When extrusion temperature is 420 ℃,the alloy could get superior intensity,tensile strength reaches 164 MPa,yield strength is up to 53 MPa and elongation rate is 21%.

关 键 词：热挤压 显微组织 退火态 挤压温度 

分 类 号：TG376.2[金属学及工艺—金属压力加工]