新型Q-P-T钢性能及其微观组织  

Property and microstructure of a novel Q-P-T steel

作　　者：胡浙梁[1] 王晓东[1] 王利[2] 戎咏华[1] 

机构地区：[1]上海交通大学材料科学与工程学院,上海200240 [2]宝山钢铁股份有限公司技术研究院,上海201900

出　　处：《材料热处理学报》2010年第4期76-80,共5页Transactions of Materials and Heat Treatment

基　　金：国家自然科学基金(50771110)

摘　　要：为了提高钢的综合强塑性能,根据徐祖耀提出的淬火-分配-回火(Q-P-T)热处理新工艺,即在Fe-Mn-Si-C钢中加入合金元素Nb和V,利用碳化物弥散析出强化,开发出了性能比Q&P钢更为优越的Q-P-T钢,证实了Q-P-T工艺设想的预期结果。通过微观结构和力学性能表征着重研究了淬火温度对残留奥氏体含量和性能的影响,从而获得了试验钢最佳的淬火温度。In order to improve ductility and toughness of steel parts,the Q-P-T steel was developed base on the quenching-partitioning-tempering（Q-P-T） heat treatment process which is proposed by Xu Zuyao.The Q-P-T steel has better mechanical properties than QP steel due to the addition of elements Nb and V into Fe-Mn-Si-C steel,which results in carbide precipitation strengthening.The effect of quenching temperature on amount of retained austenite and mechanical property of the steel was emphatically studied by microstructure characterization and mechanical property test.The optimum quenching temperature for the steel is obtained based on the experiments.

关 键 词：淬火-分配-回火(Q-P-T)钢 热处理 力学性能 残留奥氏体 淬火温度 

分 类 号：TG142.1[一般工业技术—材料科学与工程]