紫铜厚板的搅拌摩擦焊接  

Friction stir welding of thick copper plate

作　　者：贺地求[1] 易昕[1] 李再华[1] 

机构地区：[1]中南大学现代复杂装备设计与极端制造教育部重点试验室,长沙410083

出　　处：《焊接学报》2010年第4期73-76,共4页Transactions of The China Welding Institution

基　　金：国家自然科学基金资助项目(50675228)

摘　　要：采用搅拌摩擦焊接方法对厚度为25mm的T2紫铜厚板进行了单道对接焊试验,并对焊缝的微观组织、力学性能、导电特性及焊缝能谱进行了分析.结果表明,用搅拌摩擦焊方法焊接25mm厚的T2紫铜板,可得到成形美观、内部无缺陷的平板对接接头.在旋转速度为960r/min、焊接速度为70mm/min时,搅拌摩擦焊的焊接接头的抗拉强度可达到186.6MPa,搅拌摩擦焊接头的电阻率与母材基本相当.Friction stir welding is a solid-state welding technique,which may offer a new solution for thick copper plate joining.Friction stir welding of T2 copper plate,25 mm in thickness,was completed successfully by single pass welding,and the microstructure,physical property,electrical property and energy spectrum of the T2 copper joint were analyzed.The experiment results demonstrate that the appearance of the joint is good and the inner in the joint is detect-free under optimum joining conditions.When the rotating speed is 960 r/min and the welding speed is 70 mm/min,the tensile strength of the joint reaches 186.6 MPa,and the conductivity of the joint is approximately equal to that of the base metal.

关 键 词：搅拌摩擦焊 T2紫铜 厚板 性能 

分 类 号：TG115.28[金属学及工艺—物理冶金]