自密实混凝土抗氯离子渗透性及碳化性能研究  

Research on the resistance to chloride ion penetration and carbonation of SCC

作　　者：王海娜[1] 金南国[2] 王科元 

机构地区：[1]浙江工业职业技术学院,浙江绍兴312000 [2]浙江大学,浙江杭州310027 [3]宁波市北仑区白峰镇城建办,浙江宁波315831

出　　处：《混凝土》2010年第4期37-38,44,共3页Concrete

摘　　要：通过采用ATSM C1202电量法、快速碳化试验方法,研究了经配合比优化设计后的C35、C50自密实混凝土的抗氯离子渗透性能、碳化性能,并且与秦山核电站二期扩建工程处提供的同强度等级的普通混凝土进行了对比试验。研究结果表明,自密实混凝土的抗氯离子渗透性能、抗碳化性能要优于同强度等级的普通混凝土。在配合比优化设计下,自密实混凝土具有较好的抗氯离子渗透性能和抗碳化性能。By adopting the ATSM C1202 electric flux test and rapid carbonation test,we do the research on the resistance to chloride-ion pene-tration and carbonation of C35 and C50 SCC which mix design has been optimized,and do comparative test with ordinal concrete of the same in-tensity from Qinshan nuclear power plant.Researching results indicate that SCC performs better than ordinal concrete with the same intensity in the resistance to chloride-ion penetration and carbonation.By optimize mix designation,SCC has the better feature of the resistance to chloride-ion penetration and carbonation.

关 键 词：自密实混凝土 抗氯离子渗透性能 碳化性能 

分 类 号：TU528.01[建筑科学—建筑技术科学]