高温煤气脱硫剂的研究  

Development of a hot gas desulfurization sorbent

作　　者：马建平[1] 庞菊玲[1] 邓春玲[1] 

机构地区：[1]西北化工研究院,陕西西安710600

出　　处：《工业催化》2010年第4期61-65,共5页Industrial Catalysis

基　　金：国家科技攻关计划项目(97-A26-03-02-03)

摘　　要：介绍了高温煤气脱硫剂的研制、脱硫工艺条件试验、再生工艺条件试验和长周期考核试验。结果表明,以锌、锰和铁等氧化物为主成分,辅加多种助剂的高温煤气脱硫剂,可在(350～600)℃脱除煤气中的H_2S和COS,脱硫精度高,硫容大,脱硫剂脱硫后可再生。脱硫剂经22次脱硫-再生循环操作后,仍具有高脱硫性能。Development and process condition, regeneration condition and long-term tests of a hot gas desulfurization sorbent were described. The results showed that sorbents using zinc, manganese and iron as main components effectively removed HES and COS in hot gas at （350-600）℃, with high desulfurization efficiency, high sulfur capacity and regenerability. The sorbent remained highly active after 22 hours of desulfurization-regeneration cycle.