聚γ-(2-噻唑脲基)丙基倍半硅氧烷配合物的合成及磁性能  

Synthesis of Poly γ-(2-thiazole-ureido)propyltriethoxysilane Metal Complexes and Its Magnetic Properties

作　　者：吴连斌[1,2] 陈遒[2] 边高峰[2] 陈利民[2] 孙维林[1] 沈之荃[1] 

机构地区：[1]浙江大学高分子科学与工程系,杭州310027 [2]杭州师范大学有机硅化学及材料技术教育部重点实验室,杭州310012

出　　处：《高等学校化学学报》2010年第5期1056-1059,共4页Chemical Journal of Chinese Universities

基　　金：国家自然科学基金(批准号:20674071);有机硅化学及材料技术实验室开放研究基金(批准号:yjg200603);浙江省科技计划项目(批准号:2008C31005)

摘　　要：以2-氨基噻唑和异氰酸酯丙基三乙氧基硅烷为原料,合成了γ-(2-噻唑脲基)丙基三乙氧基硅烷(TUPTES),并采用溶胶-凝胶工艺制备了其过渡金属配合物(PTUPTES-Cu,PTUPTES-Ni).用红外光谱、核磁共振谱、扫描电镜和能谱等分析手段进行了表征.磁性测试结果表明,两种配合物在低温下都是较好的软铁磁体,其居里-外斯温度分别为119和75 K.γ-（2-Thiazole-Ureido）propyltriethoxysilane（TUPTES） was firstly sythesized from 2-aminothiazole and γ-isocyanatopropyltriethoxysilane.The complexes PTUPTES-Cu and PTUPTES-Ni were prepared by sol-gel technology,respectively.Their properties were characterized by IR,1H NMR,SEM and EDS.The magnetic behavior of the complexes were measured,which indicates that both of them were good soft ferromagnet at low temperature,the Curie-Weiss temperature is gained（T=119,75 K）,respectively.

关 键 词：聚倍半硅氧烷 金属配合物 磁性能 

分 类 号：O631[理学—高分子化学]