稀土La对激冷铸铁凸轮轴组织性能的影响  

Effect of Rare Earth La on Microstructure and Properties of Chilled Iron Camshaft

作　　者：米国发[1] 何斌锋[1] 

机构地区：[1]河南理工大学材料科学与工程学院,河南焦作454000

出　　处：《热加工工艺》2010年第9期12-15,共4页Hot Working Technology

基　　金：河南省杰出人才创新基金(0621000700)

摘　　要：在激冷铸铁凸轮轴生产过程中适当地加入孕育剂可以有效减小桃尖处白口深度。研究了稀土La对凸轮轴组织性能的影响。实验结果显示,稀土La能有效减小白口深度,提高铸件的力学性能;在轴颈部位碳化物≤15%的条件下,随着稀土La加入量的增加,形成石墨能力越来越强,石墨长度也增加,并且以A型石墨为主;同时,增加稀土La加入量能降低铁液激冷敏感性,不利于凸轮轴生产控制。Proper inoculant amount is used to reduce the chill depth of cam during the production of chilled iron camshaft.The effect of rare earth La on microstructure and properties of the chilled iron camshaft was studied.The results show that rare earth La can efficiently decrease the chilled depth,but increase the mechanical properties;moreover,when the bearing location of camshaft contains less than 15% carbonide,increasing the rare earth La adding contents may cause the graphite amount increasing and the dimension of graphite growing up,a large scale of A-type graphite are obtained.At the meantime,the increase of rare earth La content decreases the chilled sensibility of the molten metal,which goes against production control.

关 键 词：合金铸铁 凸轮轴 稀土La 激冷层深度和硬度 

分 类 号：TG243[金属学及工艺—铸造]