聚1-十二烯减阻剂粘均分子量与减阻率关系的研究  

Research on Relation of Viscosity-average Molecular Weight and Resistance of Poly-1-Dodecene Drag Reducer

作　　者：林颖[1] 李惠萍[1] 胡子召[1] 桑伟[1] 饶小峰[1] 

机构地区：[1]新疆大学化学化工学院,新疆乌鲁木齐830008

出　　处：《辽宁化工》2010年第5期463-466,共4页Liaoning Chemical Industry

基　　金：2006年新疆维吾尔自治区高等学校科研计划项目(项目编号:060112)

摘　　要：用室内模拟环道评价装置测定了聚1-十二烯减阻剂的减阻率,乌氏粘度计测定了聚1-十二烯减阻剂的特性粘数,并通过25℃下聚辛烯的Mark-Houwink方程估算了样品的粘均分子量,最后比较发现,减阻率随粘均分子量增大而增加,但粘均分子量过大时,减阻率反而减小。The resistance of poly-1-dodecene drag reducer was measured by the simulative loop evaluation apparatus,and the intrinsic viscosity of poly-1-dodecene was measured by the Ubbelodhe visco-meter.Then,viscosity-average molecular weights of samples were evaluated by the Mark-Houwink equation of poly-1-octene at 25℃.At last,compared with the results,it was found out that the resistance of poly-1-dodecene increased with the increase of the viscosity-average molecular weight,but the drag-reducing efficiency would decrease when the viscosity-average molecular weight was too big.

关 键 词：聚1-十二烯 减阻剂 减阻率 特性粘数 

分 类 号：TQ325.1[化学工程—合成树脂塑料工业]