Synthesis of Li_2Fe_(0.9)Mn_(0.1)SiO_4/C composites using glucose as carbon source  

作　　者：彭春丽 张佳峰 曹璇 张宝 

机构地区：[1]School of Metallurgical Science and Engineering, Central South University

出　　处：《Journal of Central South University》2010年第3期504-508,共5页中南大学学报（英文版）

基　　金：Project(50302016) supported by the National Natural Science Foundation of China

摘　　要：Li2Fe0.9Mn0.1SiO4/C composites were synthesized by using X-ray diffractometry （XRD）, scanning electron microscopy （SEM） glucose as carbon source. The samples were characterized by and electrochemical measurements. All Li2Fe0.9Mn0.1SiO4/C composites are of the similar crystal structure. With increasing the carbon content in the range of 5%-20% （mass fraction）, the diffraction peaks in XRD patterns broaden and the particle sizes and the tap density of samples decrease. The Li2Fe0.9Mn0.1SiO4/C composites with carbon content of 14.12% show excellent electrochemical performances with an initial discharge capacity of 154.7 mA.h/g at C/16 rate, and the capacity retention remains 92.2% after 30 cycles.Li_2Fe_(0.9)Mn_(0.1)SiO_4/C composites were synthesized by using glucose as carbon source. The samples were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and electrochemical measurements. All Li_2Fe_(0.9)Mn_(0.1)SiO_4/C composites are of the similar crystal structure. With increasing the carbon content in the range of 5%-20% (mass fraction), the diffraction peaks in XRD patterns broaden and the particle sizes and the tap density of samples decrease. The Li_2Fe_(0.9)Mn_(0.1)SiO_4/C composites with carbon content of 14.12% show excellent electrochemical performances with an initial discharge capacity of 154.7 mA·h/g at C/16 rate, and the capacity retention remains 92.2% after 30 cycles.

关 键 词：lithium ion batteries CATHODE lithium iron orthosilicate carbon coating 

分 类 号：TB333[一般工业技术—材料科学与工程]