Ni_(55)Fe_(18)Ga_(27)磁性形状记忆合金的组织结构与马氏体相变  

Microstructure and martensitic transformation of Ni_(55)Fe_(18)Ga_(27) magnetic shape memory alloy

作　　者：孙瑞涛[1] 韩明[1] 王立东[1] 于忠辉[1] 张雯[1] 庞年斌[1] 

机构地区：[1]山东理工大学机械工程学院,山东淄博255049

出　　处：《山东理工大学学报（自然科学版）》2009年第4期38-40,共3页Journal of Shandong University of Technology:Natural Science Edition

基　　金：山东省自然科学基金资助项目(Y2006F61);教育部留学回国人员科研启动基金资助项目

摘　　要：采用光学显微镜、差示扫描量热仪、X射线衍射仪、透射电子显微镜等对Ni55Fe18Ga27磁性形状记忆合金的组织结构与马氏体相变行为进行了研究.实验结果表明铸态合金的马氏体转变温度在室温以上,而且马氏体相呈规则排列的板条状;研究还表明其稳态马氏体为14M型单斜调制结构,晶格参数:a=0.4151nm、b=0.5141nmc、=2.9460nm、β=91.13°.The microstructure and martensitic transformation of Ni55Fe18Ga27 magnetic shape memory alloy were investigated by optical microscope,XRD,DSC and TEM.Experimental results showed that the microstructure of as-melted alloys was composed of martensitic phase at room temperature.The crystal structure of the martensite phase was determined to be 14M.The lattice parameter are a= 0.415 1nm,b= 0.514 1nm,c= 2.946 0nm,β=91.13°.

关 键 词：Ni-Fe-Ga 磁性形状记忆合金 组织结构 马氏体相变 

分 类 号：TG111.92[金属学及工艺—物理冶金] TG139.6[金属学及工艺—金属学]