La_(0.85)K_(0.15)MnO_3多晶纳米颗粒磁制冷材料的制备  

Synthesis of La_(0.85)K_(0.15)MnO_3 Polycrystalline Nanoparticles Magnetic Refrigerant

作　　者：李丽荣[1,2] 赵娟[2] 王贵[2] 

机构地区：[1]内蒙古科技大学数理与生物工程学院,包头014010 [2]广东海洋大学工程学院,广州510000

出　　处：《金属功能材料》2010年第3期13-15,共3页Metallic Functional Materials

基　　金：国家自然科学基金(基金号:50672015)

摘　　要：采用非晶态多核配合的方法在800℃制备出La0.85K0.15MnO3纳米颗粒,用XRD、HRTEM和PPMS等手段对纳米颗粒的微观结构和磁性能进行研究。XRD和ED分析表明,所有样品都具有单相钙钛矿结构;样品的M-T曲线研究结果表明,La0.85K0.15MnO3纳米颗粒的居里温度TC为242.65 K。The nanosized particles of La0.85K0.15MnO3 perovskite-type oxides was sucessfully synthesized at relatively low calcinated temperature（800℃） for 10 h using amorphous heteronuclear complexing method.The microstructure of nanoparticles were studied by X-ray diffraction（XRD） and high resolution transmission electronmicroscopy（HRTEM） and the magnetic properties were investigated by physical property measurement system（PPMS）.The X-ray diffraction（XRD） and electron diffraction（ED） reveal that the resulting product is of pure single-phase rhombohedral structure.The Curie temperature（TC） of La0.85K0.15MnO3 polycrystalline nanoparticles was determined by M-T curves,and the Curie temperature TC is about 242.65 K.

关 键 词：居里温度 纳米颗粒 La0.85K0.15MnO3 

分 类 号：TM271[一般工业技术—材料科学与工程]