Mn元素对纳米晶Fe_3Al材料的力学性能的影响  

Effect of Mn Element on Mechanical Properties of Bulk Nanocrystalline Fe_3Al Prepared by Aluminothermic Reaction

作　　者：喇培清[1] 程春杰[1] 赵阳[1] 

机构地区：[1]兰州理工大学有色金属新材料国家重点实验室,甘肃兰州730050

出　　处：《金属功能材料》2010年第3期53-56,共4页Metallic Functional Materials

基　　金：国家自然科学基金(50674051)

摘　　要：研究了合金元素Mn不同含量对铝热反应熔化法制备的块体纳米晶Fe3Al材料力学性能的影响,结果表明当Mn添加到纳米晶Fe3Al材料中,对其压缩屈服强度和抗弯强度影响显著。加Mn 10%时,纳米晶Fe3Al材料的力学性能得到很大提高,使材料由脆性材料向塑性材料转变,大幅度提高了其压缩屈服强度,而且提高了抗弯屈服强度。含Mn 10 wt%的材料具有最佳的力学性能是由于其具有最小的纳米晶粒尺寸。对含Mn 10 wt%的材料在不同加载速率下进行的压缩性能试验研究表明:材料的压缩屈服强度随加载速率的增大而降低。Nanocrystalline Fe3Al materials were prepared by aluminothermic reaction.The results show that the addition of Mn in nanocrystalline Fe3Al obviously affects compressive strength and bending strength.When the addition of Mn is 10 wt%,due to changing from the brittle material to the plastic material,the mechanical properties of nanocrystalline Fe3Al are improved well.Under different loading rate,compression yield strength reduces with increase loading rate.

关 键 词：纳米晶Fe3Al 抗弯强度 抗压强度 