CuNiCoCrBeZr合金强化工艺与组织性能研究  

Study on Strengthening Technology of CuNiCoCrBeZr Alloy and Its Microstructure and Properties

作　　者：杨丹[1] 曾刚[1] 谢春生[1] 

机构地区：[1]江苏科技大学材料科学与工程学院,江苏镇江212003

出　　处：《热加工工艺》2010年第10期164-168,共5页Hot Working Technology

基　　金：江苏省科技厅重大科技攻关资助项目(BE200768)

摘　　要：对CuNiCoCrBeZr合金进行了一系列的热处理强化工艺试验。结果表明,该合金经940℃×1.5 h固溶+30%冷变形+490℃×3 h时效处理后,其硬度为253 HB,导电率为57.76%IACS,室温下抗拉强度903 MPa,屈服强度861 MPa,伸长率16.24%,其物理性能和力学性能均能满足服役条件苛刻的超(超)临界汽轮发电机转子槽楔的使用要求。The strengthening technology of CuNiCoCrBeZr alloy was researched by heat treatment and cold deformation.The results show that,after solution treatment at 940 ℃ for 1.5 h,cold deformation of 30%,then aging at 490 ℃ for 3 h,the hardness and electric conductivity of the CuNiCoCrBeZr alloy can achieve 253 HB and 57.76 %IACS,respectively,and its strength（σb and σ0.2） and elongation（δ） can reach 903 MPa,861 MPa and 16.24%,respectively at ambient temperature.The mechanical and physical properties of the alloy can meet the technical requirement of slot wedge used in ultra supercritical generator rotor.

关 键 词：CuNiCoCrBeZr合金 时效处理 硬度 导电率 

分 类 号：TG156.92[金属学及工艺—热处理]