添加TiC对WC-Co基硬质合金组织和力学性能的影响  

Effect of TiC on Microstructures and Mechanical Properties of WC-Co-based Carbides

作　　者：王丽利[1] 李海艳[1] 刘宁[1] 

机构地区：[1]合肥工业大学材料科学与工程学院,安徽合肥230009

出　　处：《热处理》2010年第3期25-30,共6页Heat Treatment

摘　　要：采用粉末冶金工艺制备了不同TiC含量的WC-Ti-Co硬质合金。测定了常温力学性能,并采用XRD、SEM和EDS等方法分析了材料的相结构、组织形貌。试验结果表明,添加少量细晶粒TiC可以细化硬质合金的显微组织,提高其相对密度和硬度,但降低合金的断裂韧度。当TiC添加量为1.2%时,材料的综合力学性能最佳。WC-TiC-Co carbides with different contents of TiC were prepared by a powder metallurgy procedure. The mechanical properties were measured at normal temperature, and the phase structure and microstructure were studied by using XRD, SEM and EDS. The results show that so far as the carbides are concerned, addion of a small amount of fine grain TiC will refine their microstructure and increase their relative density and hardness while their fracture toughness will be reduced. Besides, the carbide will have the best mechanical properties when TiC content is 1.2%.

关 键 词：硬质合金 TIC 显微组织 力学性能 

分 类 号：TG135.1[一般工业技术—材料科学与工程]