聚苯胺/环氧树脂防静电涂料的研制  

Development research of electrostatic conductive coating of polyaniline/epoxy resin

作　　者：易波[1] 王群[1] 郭红霞[1] 

机构地区：[1]北京工业大学材料科学与工程学院,北京100124

出　　处：《化工新型材料》2010年第6期112-114,共3页New Chemical Materials

摘　　要：研究了采用化学氧化聚合法直接合成聚苯胺/环氧树脂防静电涂料的制备工艺。讨论了苯胺与环氧的质量比、氧化剂浓度、反应物酸浓度等反应条件对聚苯胺/环氧树脂防静电涂料性能的影响。结果表明,较佳的工艺条件为:苯胺与环氧树脂的质量比为0.3,盐酸浓度为2mol/L,氧化剂与苯胺的摩尔比为0.5时,制成的聚苯胺/环氧树脂防静电涂料相对较好,各项指标可满足防静电涂料的要求。Studied one method of electrostatic conductive coating of polyaniline/epoxy resin which was direct composed by the chemical oxidation polymerization.The effect of reactive conditions on the polyaniline/epoxy composite coating such as mass ratio of aniline and epoxy,dosage of oxidantand and acid concentration of reactants were discussed.The result showed that the optimized technologic conditions were as follows： the mass ratio of aniline and epoxy was 0.3,the acid concentration of reactants was 2mol/L,the molar ration of ammonium persulfate and aniline was 0.5.The coating films made under above conditions were better,and it met the needs of electrostatic conductive coatings.

关 键 词：聚苯胺 环氧树脂 防静电涂料 

分 类 号：TQ637[化学工程—精细化工]