Research on continuous core-filling casting forming process of copper-clad aluminum bimetal composite material  

作　　者：He LIANG Zhiyong XUE Chunjing WU Qing LIU Yuan WU 

机构地区：[1]School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China [2]School of Energy and Power Engineering, North China Electric Power University, Beijing 100083, China

出　　处：《Acta Metallurgica Sinica(English Letters)》2010年第3期206-214,共9页金属学报（英文版）

基　　金：supported by the National Natural Science Foundation of China (No.50774009);the National High Technology Research and Development Program of China (No.2009AA03Z532)

摘　　要：A single forming equipment of bimetal continuous core-filling casting was designed and manufactured for the purpose of developing copper-aluminum composite materials.The characteristics of the equipment were as follows：the crystallizer composed of water jacket copper sleeve in which graphite sleeve was set, two melting furnaces with different diameters vertically distributed, the low furnace of melting copper linked with the crystallizer, continuous casting and core-filling proceeded at the meantime.The rational processing parameters were determined through a series of experiments：contact length from down crucible to water-cooling cupreous crystallizer, 20 mm;length of recooling spray jet under crystallizer, 95 mm;temperature of copper and aluminum, 1250-1320℃ and 700℃ respectively;pulling rate, 16 mm/min.The qualified copper-clad aluminum composite rods, the external and inner diameter of which was 40 mm and 24 mm respectively, could be drawn successfully on that basis.Tested by hydrostatic extrusion and drawing process, the boss ratios of the copperclad aluminum composite rods were maintained a relatively stable scope of about 0.59-0.65, which was not obviously changed by subsequent plastic processing.A single forming equipment of bimetal continuous core-filling casting was designed and manufactured for the purpose of developing copper-aluminum composite materials.The characteristics of the equipment were as follows：the crystallizer composed of water jacket copper sleeve in which graphite sleeve was set, two melting furnaces with different diameters vertically distributed, the low furnace of melting copper linked with the crystallizer, continuous casting and core-filling proceeded at the meantime.The rational processing parameters were determined through a series of experiments：contact length from down crucible to water-cooling cupreous crystallizer, 20 mm;length of recooling spray jet under crystallizer, 95 mm;temperature of copper and aluminum, 1250-1320℃ and 700℃ respectively;pulling rate, 16 mm/min.The qualified copper-clad aluminum composite rods, the external and inner diameter of which was 40 mm and 24 mm respectively, could be drawn successfully on that basis.Tested by hydrostatic extrusion and drawing process, the boss ratios of the copperclad aluminum composite rods were maintained a relatively stable scope of about 0.59-0.65, which was not obviously changed by subsequent plastic processing.

关 键 词：Continuous core-filling casting Bimetal composite rod Copperclad aluminum 

分 类 号：TG24[金属学及工艺—铸造] TB331[一般工业技术—材料科学与工程]