等离子熔覆高铬铁基涂层高温耐磨性与耐空蚀性  

High Temperature Wear Resistance and Cavitation Rosion Resistance of Plasma Cladding High-chromium Iron-base Coating

作　　者：刘均波[1] 

机构地区：[1]潍坊学院,山东潍坊261061

出　　处：《潍坊学院学报》2010年第4期1-4,56,共5页Journal of Weifang University

基　　金：山东省科技攻关项目(2007GG30003003)

摘　　要：采用等离子熔覆工艺,以Fe-Cr-C-W-Ni复合粉末为原料;在Q235钢基材表面制备了高铬铁基复合涂层。测试了涂层的高温耐磨性和耐空蚀性。结果表明,涂层中含有大量硬质耐磨相(Cr,Fe)7C3,具有较高的显微硬度,涂层在高温干滑动磨损条件下具有优异的耐磨性能和载荷特性,经44 h空蚀试验后累积的质量损失量为0Cr13Ni6Mo不锈钢的0.497倍,具有一定的耐空蚀性能。A high-chromium iron-base coating was fabricated on the surface of Q235 steel using composite powder of Fe-Cr-C-W-Ni with the optimum plasma cladding process.The high temperature wear resistance and corrosion resistance was tested.Results indicate that the coating has a great quantity hard wear resistance phase（Cr,Fe）7C3 and superior microhardness.The coating has excellent wear resistance and load character.The cumulative mass loss is only 49.7% as that of 0Cr13Ni6Mo steel after 44 hours cavitation erosion.The coating has good corrosion resistance.

关 键 词：等离子熔覆 高铬铁基涂层 高温耐磨性 耐蚀性 

分 类 号：TG174.44[金属学及工艺—金属表面处理]