Effect of TiO_2 on Synthesis of Al_4SiC_4/Al_4O_4C Composite  

作　　者：DENG Chengji KUANG Jianlei ZHU Hongxi BAI Chen 

机构地区：[1]The Key State Laboratory Breeding Base of Refractories and Ceramics, Wuhan University of Science and Technology, Wuhan 430081, China

出　　处：《China's Refractories》2010年第2期19-24,共6页中国耐火材料（英文版）

基　　金：supported by the National Science Foundation of China (NSFC) under Grant No.50772079;the National Basic Research Program of China Earmarked Research Grant No.2009CB626605

摘　　要：Al4SiC4/Al4O4C composites were synthesized based on m （ sintered clay） ： m （ active carbon ） ： m （ aluminum powder） =39： 27. 6： 33. 4, adding TiO2 powder （ anatase type, 0. 3%, 6%, 9%, respectively）, adding 〈 10% phenolic resin as binder, mixing well, pressing, drying, firing in a corundum tubular furnace in flowing argon at 1 300, 1 400, 1 500, 1 600 and 1 700℃ for 2 h, respectively. Effect of TiO2 addition on phase composition and microstructure of Al4SiC4/Al4O4C composites was investigated by TGA, chemical analysis, XRD and SEM. The results show that ： （ 1 ） Ti in the specimens loses a little in the process of firing, all residual TiO2 transforms into TiC when the firing temperature is below 1 300℃, and the formed TiC exists stably at 1 300 - 1 700 ℃; （2） the TiO2 addition has little effect on phase composition of composites ; however, when more than 3% of TiO2 is added, the formation temperature of Al4SiC4 and Al4O4C increases from 1 500 ℃ to 1 600℃ ; （ 3 ） with the concentration of Ti^4＋ increasing, Ti^4＋ may react easily with Al4SiC4 and Al4O4C forrning the finite substitution solid solution resulting in lattice defect, which leads to the decomposition of Al4SiC4 at 1 700℃, the formation of more Al4O4C short fiber, and the formation of flake Al2O3 layer on suorface of the specimen.Al4SiC4/Al4O4C composites were synthesized based on m （ sintered clay） ： m （ active carbon ） ： m （ aluminum powder） =39： 27. 6： 33. 4, adding TiO2 powder （ anatase type, 0. 3%, 6%, 9%, respectively）, adding 〈 10% phenolic resin as binder, mixing well, pressing, drying, firing in a corundum tubular furnace in flowing argon at 1 300, 1 400, 1 500, 1 600 and 1 700℃ for 2 h, respectively. Effect of TiO2 addition on phase composition and microstructure of Al4SiC4/Al4O4C composites was investigated by TGA, chemical analysis, XRD and SEM. The results show that ： （ 1 ） Ti in the specimens loses a little in the process of firing, all residual TiO2 transforms into TiC when the firing temperature is below 1 300℃, and the formed TiC exists stably at 1 300 - 1 700 ℃; （2） the TiO2 addition has little effect on phase composition of composites ; however, when more than 3% of TiO2 is added, the formation temperature of Al4SiC4 and Al4O4C increases from 1 500 ℃ to 1 600℃ ; （ 3 ） with the concentration of Ti^4＋ increasing, Ti^4＋ may react easily with Al4SiC4 and Al4O4C forrning the finite substitution solid solution resulting in lattice defect, which leads to the decomposition of Al4SiC4 at 1 700℃, the formation of more Al4O4C short fiber, and the formation of flake Al2O3 layer on suorface of the specimen.

关 键 词：Al4SiC4/Al4O4C composites Titanium oxide Solid solution MICROSTRUCTURE 

分 类 号：TQ134.11[化学工程—无机化工] TB33[一般工业技术—材料科学与工程]