Sc、Zr微合金化对Al-4Cu-1.5Mg合金组织与性能的影响  

Effects of Minor Sc and Zr Compound Alloying on Microstructure and Properties of Al-4Cu-1.5Mg Alloy

作　　者：向青春[1] 侯丽娜[1] 赵静[1] 李荣德[1] 

机构地区：[1]沈阳工业大学材料科学与工程学院

出　　处：《特种铸造及有色合金》2010年第7期611-614,共4页Special Casting & Nonferrous Alloys

基　　金：辽宁省自然科学基金资助项目(20072043)

摘　　要：试验研究了Sc和Zr复合微合金化对Al-4Cu-1.5Mg合金铸态显微组织与力学性能的影响规律。结果表明,复合添加微量Sc和Zr,有效改善了合金铸态微观组织,细化了合金晶粒,使粗大的树枝晶转变为均匀细小的等轴晶。当Sc、Zr含量分别为0.4%和0.2%时,合金的抗拉强度、屈服强度及伸长率分别为275.0MPa、176.0MPa和8.0%,与未添加合金元素的Al-4Cu-1.5Mg合金相比,抗拉强度提高了55.3%,伸长率提高了近3倍。Effects of minor Sc and Zr compound alloying on as-cast microstructure and mechanical properties of Al-4Cu-1.5Mg alloy were investigated.It is found that as-cast microstructure of the alloy is effectively improved by minor Sc and Zr compound addition,in which grain size is greatly refined and coarse dendrite is converted into uniform fine equiaxe grain.Tensile strength,yield strength and elongation of the alloy with 0.4% Sc and 0.2% Zr compound addition reach up to 275.0MPa,176.0MPa and 8.0%,respectively,increased by 55.3% in tensile strength and about 300% in elongation compared with Al-4Cu-1.5Mg matrix alloy.

关 键 词：AL-CU-MG合金 SC Zr 合金化 力学性能 

分 类 号：TG113[金属学及工艺—物理冶金]