Effects of Curing Systems on Properties of High Volume Fine Mineral Powder RPC and Appearance of Hydrates  

作　　者：刘娟红 

机构地区：[1]College of Civil and Environmental Engineering, University of Science and Technology Beijing

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2010年第4期619-623,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the Science and Technology Foundation of Beijing Municipal Education Commission (KM200410016004)

摘　　要：The effects of different curing systems on the properties of high volume fine mineral powder RPC （reactive powder concrete） and the appearances of hydrates were studied. The experimental results show that dry-heating curing promotes the development of pozzolanic reactivity of fine mineral powder; due to low cement content, 0.20 water-bind ratio and high reactive fine mineral powder content, the strength of RPC increases by around 200% after steam curing and subsequent dry-heating curing. Scanning electron microscopy and energy spectrum diagram showed that： after the high volume fine mineral powder RPC with 0.16 water-bind ratio underwent steam curing and dry-heating curing, there was no significant change in the appearance of hydrates; after the RPC with 0.20 water-bind ratio, the cement content of 150 kg/m3 and more steel slag powder underwent dry-heating curing, there was a certain change in the appearance of C-S-H, the structure of gel was more compact and was uniformly distributed, and the Ca/Si of C-S-H gel decreased from 1.41 to around 1.20.The effects of different curing systems on the properties of high volume fine mineral powder RPC （reactive powder concrete） and the appearances of hydrates were studied. The experimental results show that dry-heating curing promotes the development of pozzolanic reactivity of fine mineral powder; due to low cement content, 0.20 water-bind ratio and high reactive fine mineral powder content, the strength of RPC increases by around 200% after steam curing and subsequent dry-heating curing. Scanning electron microscopy and energy spectrum diagram showed that： after the high volume fine mineral powder RPC with 0.16 water-bind ratio underwent steam curing and dry-heating curing, there was no significant change in the appearance of hydrates; after the RPC with 0.20 water-bind ratio, the cement content of 150 kg/m3 and more steel slag powder underwent dry-heating curing, there was a certain change in the appearance of C-S-H, the structure of gel was more compact and was uniformly distributed, and the Ca/Si of C-S-H gel decreased from 1.41 to around 1.20.

关 键 词：curing system high volume fine mineral powder RPC appearance of hydrates 

分 类 号：TU528[建筑科学—建筑技术科学]