SrTiO_3:Pr^(3+),Na^+体系荧光粉的合成与性能研究  

Synthesis and Luminescent Property Research of SrTiO_3:Pr^(3+),Na^+ Phosphors

作　　者：杨英[1] 陈永杰[1] 李郎楷[1] 耿秀娟[1] 

机构地区：[1]沈阳化工大学应用化学学院,辽宁沈阳110142

出　　处：《辽宁化工》2010年第7期685-687,693,共4页Liaoning Chemical Industry

基　　金：辽宁省教育厅项目;项目编号为2009B147

摘　　要：采用高温固相法在还原气氛下制备了SrTiO3:Pr3+,Na+荧光粉。用X射线衍射分析测定了SrTiO3:Pr3+,Na+荧光粉的晶体结构,具体研究了激活剂Pr3+和助熔剂H3BO3的掺杂量对SrTiO3:Pr3+,Na+体系发光性能的影响。结果表明,SrTiO3:Pr3+,Na+荧光粉属于立方晶型;在Pr3+掺杂0.6%(与SrTiO3的摩尔比)和助熔剂H3BO3掺杂3%(与SrTiO3的摩尔比)时,此荧光粉的发光性能最佳。讨论了不同电荷补偿剂对SrTiO3:Pr3+体系激发光谱和发射光谱的影响,结果表明,Na+离子是制备Sr-TiO:Pr3+体系荧光粉的最佳电荷补偿剂。The SrTiO3：Pr3＋,Na＋ phosphors was prepared by high temperature solid-state reaction process in reducing atmosphere.The crystal structure of SrTiO3：Pr3＋,Na＋ phosphors was determined by X-ray diffractometer.The effect of dosages of Pr3＋（activating agent）and H3BO3（flux）on luminescent property of the phosphors SrTiO3：Pr3＋,Na＋ was investigated in details.The results indicate that the crystalline phase of the product belongs to cubic crystal,the luminescent property is best when molar percentages of Pr3＋ and H3BO3 are 0.6% and 3%,respectively.The effect of different charge compensators on excitation spectra and emission spectra of phosphor SrTiO3：Pr3＋ was also discussed.The results show that Na＋ is the best charge compensator for preparing the phosphor SrTiO3：Pr3＋.

关 键 词：钛酸盐 稀土 发光粉 发光性能 

分 类 号：TQ422[化学工程]