稀土大磁致伸缩材料研究  

Study on Giant Magnetostrictive Materials Containing RE

作　　者：应启明[1] 罗梓贤[1] 李东培[1] 王瑞坤[1] 姚国庆[1] 任世宽[1] 张健 孙丽红 

机构地区：[1]北京有色金属研究总院

出　　处：《稀土》1999年第1期72-74,共3页Chinese Rare Earths

基　　金：中国有色金属工业总公司重点实验室资助

摘　　要：本文采用丘克拉尔斯基法制备晶粒取向的（Ｔｂ０．２８Ｄｙ０．７２）Ｆｅ１．９５磁致伸缩材料，研究了材料的微观结构对磁致伸缩系数的影响。当（Ｔｂ０．２８Ｄｙ０．７２）Ｆｅｘ中ｘ＝１．９５时，有明显的压应力效应，在１０ＭＰａ、２００ｋＡ／ｍ时，磁致伸缩系数１５００×１０－６，当ｘ＝２时，由于出现ＲＦｅ３相，压应力效应随之减小。Czochralski techniques have been used to produce grain aligned rods of (Tb 0 28 Dy 0 72 )Fe 1.95 .The effect of microstructure on magnetostriction was investigated.It was found that there is obvious rise in the compressive magnetostrictive properties for (Tb 0 28 Dy 0 72 )Fe x ,x=1.95,under 10MPa compressive stress,the magnetostriction were 1500×10 -6 in 200kA/m.It makes appearance of intragrain RFe 3 in the matrix phase RFe 2 for (Tb 0 28 Dy 0 72 )Fe x ,x=2,which results in disappearance of the compressive stress effect.

关 键 词：稀土 磁致伸缩材料 铽 镝 铁 

分 类 号：TM27[一般工业技术—材料科学与工程]