Static Recrystallization Kinetics Model After Hot Deformation of Low-Alloy Steel Q345B  

作　　者：MA Bo PENG Yan JIA Bin LIU Yun-fei 

机构地区：[1]State Key Laboratory of Metastable Materials Science and Technology,Engineering Research Center of Rolling Equipmentand Complete Technology of Ministry of Education,Yanshan University,Qinhuangdao 066004,Hebei,China

出　　处：《Journal of Iron and Steel Research International》2010年第8期61-66,共6页

基　　金：Item Sponsored by Fok Ying Tung Education Foundation(101048);Natural Science Foundation of Hebei Province of China(E2008000835)

摘　　要：The static recrystallization behavior of low-alloy steel Q345B during double-pass hot compression deformation tests was investigated in the temperature range of 900-1000 ℃,the true strain range of 0.15-0.25 and the interpass time range of 0.5-50 s on Gleeble-3500 thermo-simulation machine.The results show that static recrystallization during the interpass time is observed.As the deformation temperature and strain increase,softening caused by static recrystallization is obvious.According to the analysis and calculation of thermo-simulation data,the static recrystallization activation energy was obtained and static recrystallization kinetics model was built.Finally,the error analysis of static recrystallization kinetics model proved that the model had good accuracy.Therefore,this model provides a theoretical basis for static recrystallization（SRX）and will contribute to the development of multipass hot rolling process,in order to control the rolling process more accurately.The static recrystallization behavior of low-alloy steel Q345B during double-pass hot compression deformation tests was investigated in the temperature range of 900-1000 ℃,the true strain range of 0.15-0.25 and the interpass time range of 0.5-50 s on Gleeble-3500 thermo-simulation machine.The results show that static recrystallization during the interpass time is observed.As the deformation temperature and strain increase,softening caused by static recrystallization is obvious.According to the analysis and calculation of thermo-simulation data,the static recrystallization activation energy was obtained and static recrystallization kinetics model was built.Finally,the error analysis of static recrystallization kinetics model proved that the model had good accuracy.Therefore,this model provides a theoretical basis for static recrystallization（SRX）and will contribute to the development of multipass hot rolling process,in order to control the rolling process more accurately.

关 键 词：Gleeble-3500 low-alloy steel static recrystallization activation energy kinetics model 

分 类 号：TG142.33[一般工业技术—材料科学与工程] TP242[金属学及工艺—金属材料]