Microstructure and Properties of Hot Rolled Ti-23Al-17Nb Alloy Sheets  

作　　者：ZHANG Jian-wei LIANG Xiao-bo CHENG Yun-jun LI Shi-qiong 

机构地区：[1]Central Iron and Steel Research Institute, Beijing 100081, China

出　　处：《Journal of Iron and Steel Research International》2010年第9期64-68,共5页

摘　　要：Microstructure and tensile properties of Ti-23Al-17Nb （at%） alloy sheets rolled in （a2 ＋ B2 ＋ O） phase field with the various heat treatments were studied. Before rolling the microstructure of the billet is B2 phase particles embedded in O phase continuity matrix. The B2 phases are deformed more greatly than a2/O phases during the same rolling step. The （a2 ＋B2） two phase equiaxed microstrueture can be obtained by solution treatment in （a2 ＋ B2） phase field. The B2 phases become the continuous matrix by recrystallization and growing up of B2 and thus anisotropy caused by rolling can be decreased. The microstructure obtained by solution treatment has better tensile properties than the microstructure gained by subsequent aging treatment in （O＋ B2） phase field because the O phases precipitate as the block structure during aging and results in the B2 matrix continuity being broken down.Microstructure and tensile properties of Ti-23Al-17Nb （at%） alloy sheets rolled in （a2 ＋ B2 ＋ O） phase field with the various heat treatments were studied. Before rolling the microstructure of the billet is B2 phase particles embedded in O phase continuity matrix. The B2 phases are deformed more greatly than a2/O phases during the same rolling step. The （a2 ＋B2） two phase equiaxed microstrueture can be obtained by solution treatment in （a2 ＋ B2） phase field. The B2 phases become the continuous matrix by recrystallization and growing up of B2 and thus anisotropy caused by rolling can be decreased. The microstructure obtained by solution treatment has better tensile properties than the microstructure gained by subsequent aging treatment in （O＋ B2） phase field because the O phases precipitate as the block structure during aging and results in the B2 matrix continuity being broken down.

关 键 词：Ti-23Al-27Nb rolled sheet microstructure PROPERTY 

分 类 号：TG131[一般工业技术—材料科学与工程] O571[金属学及工艺—合金]