86CrMoV7钢热变形奥氏体CCT图  

The CCT Curves of Hot Deformation Austenite of 86CrMoV7 Steel

作　　者：肖福仁[1] 乔桂英[1] 

机构地区：[1]燕山大学材料科学与化学工程学院

出　　处：《金属热处理》1999年第7期10-12,共3页Heat Treatment of Metals

摘　　要：采用膨胀法测定了８６ＣｒＭｏＶ７钢经Ｔ＝９００℃、ε＝１ｓ－１、ε＝０４热变形后的连续冷却转变曲线。结果表明，试验用钢在连续冷却转变过程中，只存在珠光体、马氏体转变。不发生珠光体转变的临界冷却速度为３１℃／ｓ，Ｍｓ点为１５０℃。组织分析发现，未溶碳化物可成为珠光体转变的核心。The continuously cooling transformations of 86CrMoV7 steel after T=900℃、=1s -1 、ε=0 4 hot deformation have been determined by expansion method.The results show that only exist pearlite and martensite transformation in the CCT cruves.The critical cooling rate that does not occur pearlite transformation is 3.1 ℃/s,and Ms=150℃.The microstructure analyses find that remaining carbide could be a nucleus of pearlite transformation and accelerate pearlite transformation.

关 键 词：热变形 CCT图 珠光体转变 轧辊钢 

分 类 号：TG161[金属学及工艺—热处理] TG151.2[金属学及工艺—金属学]