纳米SiO2对水性聚丙烯酸酯防火涂料性能的影响  

Influence of Nano-SiO2 on Water-borne Acrylate Fireretardant Coatings

作　　者：盛伟明[1] 王德海[1] 张周达[1] 寿晓红[1] 

机构地区：[1]浙江工业大学化学工程与材料学院

出　　处：《中国涂料》2010年第7期55-58,共4页China Coatings

摘　　要：采用乳液聚合的方法制得纳米SiO2丙烯酸酯复合乳液,通过加入膨胀型防火助剂制得水性防火涂料.利用DSC等手段对涂层结构及热性能进行了表征,探讨了涂层防火性能与纳米填料的关系.结果表明,纳米SiO2与涂层基料树脂间有明显的相互作用,并影响到涂层在受热时的热行为,3%（质量分数）的SP1型可将钢板背温由150℃降到125℃,5%（质量分数）的SS1型SiO2可将钢板背温由150℃降到110℃.Emulsion polymerization being used, we have obtained nano- SiO2 acrylate composite emulsion, and adding intumescent fire-retardant additives, we have prepared water-borne fire-retardant coatings. Adopting DSC method to token structure and thermal property, of the film. this paper discusses the relationship between coating fire-rctardant propert3, and the nano-filler, showing that significant interaction between nano- SiO2 and coatings binders is exist and the interaction will influence the thermal behavior of film when heated, SP1 SiO2 of 3%（wt） decreasing back temperature of steel plate from 150℃ to 125 and SS1 SiO2 of 5%（wt） decreasing back temperature of steel plate from 150 ℃ to 110℃.

关 键 词：水性 防火涂料 钢结构 纳米SIO2 

分 类 号：TQ637.8[化学工程—精细化工]