铸态Zn-Al合金高温拉伸变形行为  

Research of tensile deformation behavior of cast Zn-Al alloy

作　　者：许晓庆[1] 李德富[1] 郭胜利[1] 邬小萍[1] 贺金宇[1] 胡捷[1] 

机构地区：[1]北京有色金属研究总院,北京100088

出　　处：《塑性工程学报》2010年第5期118-122,共5页Journal of Plasticity Engineering

基　　金：十一五国家科技支撑计划资助项目(2009BAE71B03)

摘　　要：在SINTECH20/G拉伸试验机上对Zn-Al10-Cu2锌合金进行等温拉伸实验,研究该合金在变形温度为210℃-300℃、应变速率为0.001s^-1-0.1s^-1条件下的变形行为和拉伸力学性能。结果表明,峰值应力随温度升高而降低,随应变速率的提高而增大。通过线性回归分析,得出流变应力σ解析表达式,其中A、α和n值分别为6.63×10^12s^-1、0.0108MPa^-1和4.81,其热变形激活能Q=150.127kJ/mol。该合金在温度为300℃、应变速率为0.001s-1时,出现超塑性趋势。The tensile deformation behavior and properties of Zn-Al10-Cu2 alloy were studied by isothermal tensile experiment at 210℃-300℃ and strain rate 0.001s^-1-0.1s^-1 with simulated machine.The results show that the peak stress increases with strain rate increasing and decreases with deformation temperature increasing.The values of A,α and n in the analytical expressions of flow stress σ are fitted to be 6.63×10^12s^-1、0.0108MPa^-1 and 4.81 by linear regression analysis and optimization calculation.The hot deformation activation energy of Zn-10Al-Cu alloys during hot deformation is 150.127kJ/mol.The superplasticity trend of the alloy is occurred at 300℃ and strain rate 0.001s^-1.

关 键 词：铸态锌合金 峰值应力 拉伸 力学性能 

分 类 号：TB331[一般工业技术—材料科学与工程]