铝阳极氧化膜的界面性能与常温封闭  

The Relation Between Influence of Ions to the Interfacial Characteristics of Anodized Aluminum Porous Membrane and Cold Sealing

作　　者：旷亚非[1] 王美媛[1] 王玲[1] 

机构地区：[1]湖南大学化学化工学院

出　　处：《湖南大学学报（自然科学版）》1999年第2期24-27,31,共5页Journal of Hunan University:Natural Sciences

基　　金：机械工业部教育司基金

摘　　要：采用电渗法研究了几种电解质溶液对铝阳极氧化多孔膜界面性能的影响．结果表明，含有Ｆ－，ＳｉＯ２－３，ＰＯ３－４，Ｓ２Ｏ２－３和酒石酸根等的电解质溶液，使多孔膜的等电点ｐＨＩＥＰ由原来的９．２０分别移至３．４０，３．３０，４．３０，３．９０和３．８０，膜的带电性能发生了相应的变化．多孔膜带电性能的变化有利于常温封闭液中的金属离子进入多孔膜内，同时Ｆ－，Ｓ２Ｏ２－３还可通过与膜内Ｈ＋，Ｈ２Ｏ等的相互作用，使膜孔内ｐＨ升高，从而加速金属离子在膜内的水解沉积，促进常温封闭的进行．Influence of ions to the interfacial characteristics of the porous membrane of anodized aluminum was investigated with a electrodiatytic method.Results indicated that,when the porous membrane was pretreated with F -,SiO 2- 3,PO 3- 4,S 2O 2- 3 and C 4H 4O 2- 6,the isoelectric points pH IEP of the membrane were shifted from normal 9.20 to 3.40,3.30,4.30,3.90 and 3.80,respectively.The metal ions of cold sealing solution were easier to enter the membrane.Furthermore,the pH of the membrane holes were raised by the interaction of F -,S 2O 2- 3 and the interfacial membrane,and the metal ions were promoted to hytrolysis.

关 键 词：铝 阳极氧化 界面性能 常温封闭 多孔膜层 

分 类 号：TQ153.6[化学工程—电化学工业]