Catalytic graphitization of polyacrylonitrile(PAN)-based carbon fibers with Fe-Cr_2O_3 composite coating  

作　　者：黄振华 周海晖 彭奇龄 陈金华 旷亚非 

机构地区：[1]College of Chemistry and Chemical Engineering,Hunan University [2]State Key Laboratory of Chemo/Biosensing and Chemometrics,Hunan University

出　　处：《Transactions of Nonferrous Metals Society of China》2010年第8期1418-1423,共6页中国有色金属学报（英文版）

基　　金：Project(2006CB600903) supported by the National Basic Research Program of China

摘　　要：The process of electrodepositing Fe-Cr2O3 composite coating on polyacrylonitrile （PAN）-based carbon fibers and its catalytic graphitization were studied. Carbon fibers with and without electrodeposited Fe-Cr2O3 composite coating were heat treated at different temperatures and the structural changes were characterized by XRD, Raman spectroscopy and SEM. The results indicate that Fe-Cr2O3 composite coating exhibits a significant catalytic effect on graphitization of carbon fibers at low temperatures. When the Fe-Cr2O3-coated carbon fibers were heat treated at 1 300℃ the interlayer spacing （doo2） and ratio of relative peak area （AD/AG） reach 3.364/k and 0.34, respectively. Whereas, the extent of graphitization of pristine carbon fibers is comparatively low even after heat treatment at 2 800℃ and the values of doo2 and AD/AG are 3.414 A and 0.68, respectively. The extent of graphitization of carbon fibers increases not only with the increase of the catalyst gross but also the Cr2O3 content in Fe-Cr2O3 coating. The catalytic effect of Fe-Cr2O3 composite coating accords with the dissolution-precipitation mechanism.The process of electrodepositing Fe-Cr2O3 composite coating on polyacrylonitrile(PAN)-based carbon fibers and its catalytic graphitization were studied.Carbon fibers with and without electrodeposited Fe-Cr2O3 composite coating were heat treated at different temperatures and the structural changes were characterized by XRD,Raman spectroscopy and SEM.The results indicate that Fe-Cr2O3 composite coating exhibits a significant catalytic effect on graphitization of carbon fibers at low temperatures.When the Fe-Cr2O3-coated carbon fibers were heat treated at 1 300°C,the interlayer spacing(d002) and ratio of relative peak area(AD/AG) reach 3.364-and 0.34,respectively.Whereas,the extent of graphitization of pristine carbon fibers is comparatively low even after heat treatment at 2 800°C and the values of d002 and AD/AG are 3.414 and 0.68,respectively.The extent of graphitization of carbon fibers increases not only with the increase of the catalyst gross but also the Cr2O3 content in Fe-Cr2O3 coating.The catalytic effect of Fe-Cr2O3 composite coating accords with the dissolution precipitation mechanism.

关 键 词：carbon fiber catalytic graphitization Fe-Cr2O3 coating 

分 类 号：TQ342.74[化学工程—化纤工业]