配碳量对承钢钒钛烧结矿矿物组成及显微结构的影响  

Effect of the Carbon Content on Mineral Compositions and Mineral Phase Microscopy of Vanadium-Titanium Sinter in Chenggang

作　　者：王文山[1] 任刚[2] 孙艳芹[2] 吕庆[2] 

机构地区：[1]东北大学材料与冶金学院,辽宁沈阳110004 [2]河北理工大学冶金与能源学院,河北唐山063009

出　　处：《钢铁》2010年第10期13-17,共5页Iron and Steel

摘　　要：承德钢铁公司是河北省唯一使用钒钛磁铁矿作为主要炼铁原料的钢铁企业,但目前承钢钒钛烧结矿的强度和冶金性能不好,严重制约了高炉的顺行和炼铁系统成本的降低。采用光学显微镜研究了配碳量对承钢钒钛烧结矿显微结构的影响,对提高其烧结矿质量提供了理论依据。结果表明,随着w(C)由4.0%提高到5.5%,赤铁矿体积分数减少20%左右,磁铁矿增加,树枝状钙钛矿体积分数升高,由10%提高到25%,钒钛烧结矿的强度降低,还原性下降,RDI+3.15升高。综合来讲,过高的配碳量不利于烧结矿的质量,应控制在4.5%左右。Cheng Steel is the only company which uses vanadium-titanium magnetite as the main raw material in Hebei Province.But the lower quality of vanadium-titanium sinter is harmful to reduce the cost of production and antegrade of BF.The effects of w（C） on the vanadium-titanium sinter mineral composition and mineral phase microscopy were investigated by optical microscope to explore a favorable theoretical basis for controlling w（C）.The results show that with the increase in carbon content,the content of hematite decreases,the content of magnetite increases,the strength decreases,the RI of sinter decreases,the RDI＋3.15 of sinter will be improved.In summary,high carbon content is not conducive to quality of sinter.4.5% of carbon content is suggested.

关 键 词：钒钛烧结矿 配碳量 矿物组成 矿相显微 

分 类 号：TF046.4[冶金工程—冶金物理化学]