医用钛合金的微弧氧化膜层组织及其磨损性能  

Microstructure and its wear property of micro-arc oxidation coating on biomedical titanium alloy

作　　者：王艳玲[1] 惠松骁[1] 叶文君[1] 米绪军[1] 

机构地区：[1]北京有色金属研究总院,北京100088

出　　处：《中国有色金属学报》2010年第B10期188-192,共5页The Chinese Journal of Nonferrous Metals

摘　　要：采用微弧氧化方法对医用钛合金表面进行改性,利用X射线衍射分析(XRD)、扫描电镜(SEM)对微弧氧化膜层的表面形貌和化学成分进行分析,通过小振幅往复摩擦磨损试验测量膜层的耐磨损性能。结果表明:钛合金经过微弧氧化表面处理后,所得膜层存在不同尺寸的放电微孔,氧化膜内层相对外层较为致密;膜层主要由大量金红石型TiO_2相、非晶相SiO_2及少量锐钛矿型TiO_2相组成;与基体相比,微弧氧化膜层的初期摩擦因数从0.7降低至0.1,耐磨性提高。The coming prepared by micro-arc oxidation （MAO） on biomedical titanium alloy was investigated. The surface morphology and chemical composition of MAO coating were analyzed by X-ray diffractometry and scanning electron microscopy （SEM）. The anti-wear property of the coating was measured through small amplitude oscillatory reciprocating friction and wear test. The results show that the MAO coating has some micropores with different dimensions and the inner layer of the coating is denser compared with the outer layer. The composition of the coating comprises majority of rutile TiO2 and amorphous phase SiO2. A fraction of the composition is anatase TiO2. The preliminary friction coefficient of the coating decreases from 0.7 to 0.1. The micro-arc oxidation treatment improves the anti-wear property of the titanium alloy.

关 键 词：钛合金 医用钛合金 微弧氧化 磨损性能 

分 类 号：TG146.23[一般工业技术—材料科学与工程] TG174.45[金属学及工艺—金属材料]