预腐蚀对AF1410电子束焊接头疲劳性能的影响  

Influence of Pre-Corrosion on Fatigue Property of AF1410 EBW Joint

作　　者：余伟[1] 韩鹏[1] 吴冰[1] 

机构地区：[1]北京航空制造工程研究所高能束流加工技术重点实验室

出　　处：《航空制造技术》2010年第20期86-88,共3页Aeronautical Manufacturing Technology

摘　　要：AF1410钢是一种新型的超高强度钢,是船舶、航空飞机的重要承力构件首选材料之一。这些承力构件通常采用电子束焊接,针对这些构件服役条件的特殊性,本课题提出了盐水预腐蚀对疲劳性能影响的试验方法,验证了AF1410钢电子束焊接接头在特殊环境下的可靠性。测试了不同腐蚀时间、不同载荷下AF1410钢电子束焊接接头在盐水中的腐蚀疲劳性能,对获取的大量试验数据进行了深入分析。试验结果表明,预腐蚀对AF1410钢电子束焊接接头的疲劳寿命有一定影响,会降低焊接构件在交变载荷下的使用寿命。AF1410 steel is a new type super intension steel, which is suited to manufacture key parts of ship and aircraft. Usually, these parts are welded by electron beam welding （EBW）. In order to verify the reliability of AF1410 steel EBW joint, brine pre-corrosion fatigue life detection method is introduced. After different brine corrosion time, the fatigue lifes of EBW joints of AF1410 steel are obtained under different cycle loading. Through studying these test data, it can be found that pre-corrosion will decrease the fatigue life olAF1410 steel EBW joints.

关 键 词：AF1410钢 电子束焊接 预腐蚀 疲劳性能 

分 类 号：TG407[金属学及工艺—焊接] TG172