ZIF-68金属有机多孔骨架材料的催化性能  

CATALYTIC PERFORMANCE OF METAL-ORGANIC FRAMEWORK ZIF-68

作　　者：任蕾[1] 范彬彬[1] 王佳[1] 张鹏飞[1] 窦涛[1,2] 

机构地区：[1]太原理工大学精细化工研究所,山西太原030024 [2]中国石油催化重点实验室,北京102249

出　　处：《石油学报（石油加工）》2010年第5期673-676,共4页Acta Petrolei Sinica(Petroleum Processing Section)

基　　金：国家自然科学基金项目(20373039)资助

摘　　要：以咪唑类金属有机多孔骨架材料ZIF-68为载体,采用浸渍法制备了Pd/ZIF-68负载型催化剂。采用XRD、N2吸附-脱附等方法对Pd/ZIF-68进行了表征,并考察了Pd/ZIF-68在苯乙烯选择加氢反应中的催化性能及抗氮、抗硫性能。结果表明,Pd/ZIF-68可有效地催化苯乙烯选择加氢反应,并呈现出良好的抗氮性能。Pd/ZIF-68的催化活性与反应时间、反应温度、反应压力及Pd的负载量等有着密切关系。ZIF-68（Zeolitic imidazolate frameworks） was selected as support for preparing Pd/ZIF-68.The prepared Pd/ZIF-68 was characterized by XRD,N2adsorption-desorption.The catalytic performance of Pd/ZIF-68 was also investigated in styrene hydrogenation.The results showed that Pd/ZIF-68 could effectively catalyze styrene hydrogenation and had higher nitrogen resistance ability.Reaction conditions,including H2pressure,reaction temperature,reaction time and the Pd loading had great influence on the catalytic hydrogenation activity of the catalyst.

关 键 词：金属有机多孔骨架材料 ZIF-68 苯乙烯加氢 

分 类 号：TQ032[化学工程]