低温燃烧合成法制备纳米氧化镧  被引量:9

Preparation of Nanometer Lanthanum Oxide Powder by Low-temperature Combustion Synthesis Method

在线阅读下载全文

作  者:张海瑞 储刚[1] 周莉[1] 周鑫[1] 曾丽瑛[1] 

机构地区:[1]辽宁石油化工大学化学与材料科学学院,抚顺113001

出  处:《人工晶体学报》2010年第5期1286-1291,共6页Journal of Synthetic Crystals

基  金:国家高技术研究发展计划(863计划)(2005AA001510)

摘  要:以六水硝酸镧、一水柠檬酸为原料,利用低温燃烧合成法制备了纳米La2O3粉体。利用XRD、TG-DTA和TEM等测试方法对干凝胶热分解过程及最终形成的纳米La2O3粉体进行了表征,并研究了前驱体溶液的pH值、物质的量配比、煅烧温度、煅烧时间对粉体粒径和形貌的影响。实验结果表明,在溶液的pH=2,La(NO3)3·6H2O∶C6H8O7·H2O=6∶7,煅烧温度在700-900℃,煅烧时间为1.5 h时,可获得粒径均匀的纳米La2O3粉体,且所得产物的粒径范围为50-100 nm。Using La(NO3)3·6H2O and citric acid as raw materials,nanometer lanthanum oxide powders was prepared by low-temperature combustion synthesis method.The as-prepared powders was characterized by means of XRD,TG-DTA and TEM.The influence of pH value of the precursor solution,molar ratios,calcining temperature,calcining time etc on particle size of powders and the morphology were investigated.The experiment results show that nano-La2O3 powders with uniform grain size of 50-100 nm on the average grain diameter was prepared under the conditions of pH value of 2,mole ratio of 6∶7 of La(NO3)3· 6H2O∶C6H8O7· H2O,calcining temperature of 700-900 ℃,calcining time of 1.5 h.

关 键 词:低温燃烧合成 纳米氧化镧 粒径 

分 类 号:O64[理学—物理化学]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象