无卤阻燃高抗冲聚苯乙烯材料阻燃性能的研究  

Study on Flame Retardancy of Halogen-free Retardants Retarded High Impact Polystyrene

作　　者：林春平[1] 吴大鸣[1] 刘颖[1] 郑秀婷[1] 

机构地区：[1]北京化工大学塑料机械与塑料工程研究所,北京100029

出　　处：《中国塑料》2010年第10期28-32,共5页China Plastics

基　　金："十一五"国家科技支撑计划重点项目(2006BAE03B05-3);中央高校基本科研业务费专项资金资助(QN0910)

摘　　要：以微胶囊红磷(MRP)母料和聚苯醚(PPO)为复配阻燃剂,采用熔融共混法制备了无卤阻燃高抗冲聚苯乙烯(PS-HI)材料,采用氧指数、垂直燃烧法和热失重分析研究了复配阻燃剂对PS-HI的阻燃作用,对阻燃PS-HI热失重后的残留物进行红外分析。结果表明,10%的MRP母料和18%的PPO复配,可以使PS-HI的氧指数提高到34%,垂直燃烧级别达到FV-0(1.5 mm),MRP与PPO之间存在协同阻燃效应,复配阻燃剂的作用机理为凝聚相阻燃机理。Masterbatch of micro-capsulated red phosphorus （MRP） and polyphenylene oxide （PPO） were compounded forming a flame retardant, which was applied in high impact polystyrene （PS HI） via melt blending. The flame retardant effect was studied through oxygen index, vertical burning test, and thermal gravimetric analysis. Residue collected during thermal gravirnetric analysis was characterized by Fourier transform infrared spectroscopy. It was revealed that with the incorporation of the compound flame retardant, when the contents of MRP and PPO were 10 % and 18%, respectively, PS-HI displayed an oxygen index of 34 % and a vertical burning level of FV-0 （1.5 mm）. There was a synergetic effect between MRP and PPO, and the flame retardant acted mainly in the condensed phase.

关 键 词：高抗冲聚苯乙烯 无卤阻燃剂 微胶囊红磷 聚苯醚 协同阻燃 阻燃性能 

分 类 号：TQ325.2[化学工程—合成树脂塑料工业]