双组分低密度聚酯型聚氨酯鞋底原液的研制  

Preparation of Two-Component Low Density Polyester Type Polyurethane Sole System

作　　者：蔡福泉 江吉旺[2] 田志胜 熊静[2] 

机构地区：[1]温州市登达化工有限公司,325000 [2]温州大学化学与材料工程学院,325035

出　　处：《聚氨酯工业》2010年第5期28-31,共4页Polyurethane Industry

基　　金：浙江省新苗计划项目资助;浙江省科技厅项目资助(No:2008C21034);浙江省科技厅项目资助(No:2009C33059)

摘　　要：以己二酸、乙二醇、一缩二乙二醇和自制的复合催化剂等为原料,合成了聚酯多元醇;进一步以自制的聚酯多元醇和MD I等为原料,制备了双组分低密度聚酯型聚氨酯鞋底原液,并讨论了密度、温度等对鞋底原液性能的影响。应用结果表明,PU鞋底的撕裂强度、耐折性、拉伸强度等性能指标均达到预期的要求。The polyester polyol was prepared by adipic acid, glycol, diethylene glycol and the self-made composite catalyst. The double component low density sole system of the polyester-type polyurethane was prepared from the self-made polyester polyol, MDI and so on. The effects of density, temperature on performanee.of the PU sole system were also discussed. The test results showed that main performance index of PU soles such as tearing strength, folding resistance, tensile strength and so on had achieved the anticipated requirements.

关 键 词：低密度 聚酯多元醇 聚氨酯鞋底原液 

分 类 号：TQ323.8[化学工程—合成树脂塑料工业]