Effect of ZnO content on magnetic characteristics in low harmonic distortion MnZn ferrite

作　　者：戴勇飞 邵峰[1] 

机构地区：[1]天通控股股份有限公司,浙江海宁314400

出　　处：《电子元件与材料》2010年第11期52-54,共3页Electronic Components And Materials

基　　金：国家"863"计划资助项目(No.2008AA03Z407)

摘　　要：为了提高非对称数字用户线(ADSL)接入系统的网络传输质量,采用传统氧化物陶瓷工艺制备了低失真MnZn铁氧体,并研究了在Fe2O3含量不变的前提下,ZnO含量与其磁特性的关系。结果表明:适量的ZnO可以提高起始磁导率μi,降低磁滞常数ηB。随着ZnO含量的增加,μi值先增大后减少,截止频率fr先减少后增加。当x(ZnO)为23%时,其μi=8 100,ηB=0.42×10–6/mT。Low harmonic distortion MnZn ferrites were prepared by conventional oxide ceramic process to improve the network transmission quality of asymmetric digital subscriber line（ADSL） access system.The relationship of magnetic characteristic and ZnO content in low harmonic distortion MnZn ferrite was investigated with constant content of Fe2O3.The results show that the initial permeability μi and hysteresis material constant ηB are improved with appropriate amount of ZnO.The μi initially increases and then decreases,the cut-off frequency fr initially decreases and then increases with the increase of ZnO content.Initial permeability and hysteresis material constant of the low harmonic distortion MnZn ferrite material are 8 100 and 0.42×10^–6/mT respectively,when x（ZnO） reachs 23%.

关 键 词：MNZN铁氧体 低失真 磁滞常数 ZnO含量 

分 类 号：TM277[一般工业技术—材料科学与工程]