钢表面化学镀Ni/金刚石复合膜后淬火回火工艺的研究  

Study on Quenching-tempering Technology for Low Carbon Steel Coated with Electroless Nickel-diamond Film

作　　者：廖一峰[1] 彭樟林[2] 

机构地区：[1]韶关学院物理与机电学院,广东韶关512005 [2]浙江林学院工程学院,浙江临安311300

出　　处：《热加工工艺》2010年第20期158-160,共3页Hot Working Technology

基　　金：韶关市科技计划资助项目(313-140379);江门市科技计划资助项目(2008-2009)

摘　　要：通过化学镀方法在钢表面获得了镍-磷-金刚石复合膜,并对镀有复合膜的钢进行淬火及回火热处理,研究了淬火温度(450、650、850℃)和回火温度(200℃)对复合膜组织和性能的影响。用SEM、X-射线衍射仪、刻痕法和盐水浸蚀法研究了不同工艺条件下复合膜的形貌、结构、附着性和耐蚀性。结果表明,热处理后,纳米金刚石颗粒在复合膜中的分布更均匀;硬度由热处理前的505 HV增大到909.9 HV;在w(NaCl)=10%溶液中常温下放置48 h,镀层无腐蚀痕迹;在19.6 N的载荷作用下,复合膜无脱落,表明附着力良好。The composite film of Ni-P-diamond on low carbon steel surface was prepared by chemical plating,and then treated by quenching and tempering.The effects of quenching temperature（450,650,850 ℃） and tempering temperature（200 ℃） on microstructure and properties of the composite film were studied.The morphology,microstructure,adhesion and wearing corrosion of the composite film were investigated with SEM,XRD,notch and brine corrosion.The results show that after heat treatment,the distribution of nano-diamond particles is more uniform within the composite films.The microhardness increases from 505 HV to 909.9 HV.Immersion test in NaCl solution for48 h at room temperature didn＇t find visible corrosion spot.The composite film remains integrated without any peel-off underscratch load of 19.6 N.

关 键 词：化学镀镍 复合膜 淬火 回火 附着性能 

分 类 号：TG174.44[金属学及工艺—金属表面处理]