Polyimide-silver nanocomposite containing phosphine oxide moieties in the main chain:Synthesis and properties  

作　　者：Khalil Faghihi Mohsen Hajibeygi Meisam Shabanian 

机构地区：[1]Organic Polymer Research Laboratory,Department of Chemistry,Faculty of Science,Arak University

出　　处：《Chinese Chemical Letters》2010年第11期1387-1390,共4页中国化学快报（英文版）

摘　　要：New flame-retardant polyimide-silver nanocomposite containing phosphine oxide moiety in the main chain was synthesized by a convenient ultraviolet irradiation technique.A precursor such as AgNO_3 was used as the source of the silver particles.Polyimide 6 as a source of polymer was synthesized by polycondensation reaction of bis（3-aminophenyl） phenyl phosphine oxide 4 with pyromellitic anhydride 5 in the presence of iso-quinoline as base and in m-cresol solution.The resulting composite film was characterized by FTIR spectroscopy,X-ray diffraction（XRD）,transmission electron microscopy（TEM）,thermogravimetry（TGA） and differential scanning calorimetry（DSC）.The average size of the nanometer Ag particles is about 10 nm.The temperature of 5 and 10%weight loss and also the char yield at 600℃of polyimide-silver nanocomposite 6a were higher than the pure PI 6.New flame-retardant polyimide-silver nanocomposite containing phosphine oxide moiety in the main chain was synthesized by a convenient ultraviolet irradiation technique.A precursor such as AgNO_3 was used as the source of the silver particles.Polyimide 6 as a source of polymer was synthesized by polycondensation reaction of bis（3-aminophenyl） phenyl phosphine oxide 4 with pyromellitic anhydride 5 in the presence of iso-quinoline as base and in m-cresol solution.The resulting composite film was characterized by FTIR spectroscopy,X-ray diffraction（XRD）,transmission electron microscopy（TEM）,thermogravimetry（TGA） and differential scanning calorimetry（DSC）.The average size of the nanometer Ag particles is about 10 nm.The temperature of 5 and 10%weight loss and also the char yield at 600℃of polyimide-silver nanocomposite 6a were higher than the pure PI 6.

关 键 词：FLAME-RETARDANT Polyimide-silver nanocomposite Phosphine oxide moiety 

分 类 号：TB383.1[一般工业技术—材料科学与工程]