SEBS/蒙脱土复合材料结构及热性能研究  

Study on Structure and Thermal Property of SEBS/ Montmorillonite Composite

作　　者：李晓燕[1] 王霞[1] 

机构地区：[1]上海理工大学材料科学与工程学院,上海230009

出　　处：《塑料科技》2010年第12期43-47,共5页Plastics Science and Technology

基　　金：上海理工大学博士启动基金资助项目(10D305)

摘　　要：采用十二烷基三苯基溴化膦(DTPB)改性钠基蒙脱土(Na+-MMT),利用熔融插层法制备氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物(SEBS)/蒙脱土复合材料。采用X射线衍射仪、红外光谱仪、场发射扫描电镜、热重分析仪对样品进行结构表征和性能测试,比较不同有机化蒙脱土(OMMT)对SEBS/OMMT复合材料的影响。结果表明:无论是MMT还是OMMT都起到了阻止SEBS热失重进程的发展,且携带苯基的DTPB有机改性剂有利于OMMT与SEBS复合材料的相容性。Dodecyltriphenylphosphonium bromide （DTPB） was used as organic intercalating agent to modify sodium montmorillonite （Na^＋-MMT）, and hydrogenated styrene-butylenes-styrene （SEBS）/MMT composites were prepared by means of melt intercalation method. The samples were characterized with XRD, FTIR, FESEM and TGA, and the influences of different organic montmorillonite （OMMT） for SEBS/OMMT composites were compared. The results show that MMT and OMMT can prevent thermo gravimetric progress of SEBS, and DTPB has a good effect on the compatibility between OMMT and SEBS.

关 键 词：氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物 十二烷基三苯基溴化膦 有机化蒙脱土 热失重分析 

分 类 号：TQ334.3[化学工程—橡胶工业] TQ330.38