以[M(DETA)_2)](n＋)(M=Cu(2＋),Ni(2＋),Co(3＋))为客体的MnPS_3夹层化合物的合成、结构表征与磁性研究(英文)  

Intercalation of Cationic [M(DETA)_2)]^(n+)(M=Cu^(2+),Ni^(2+),Co^(3+)) into Layered MnPS_3: Synthesis,Characterization and Magnetic Properties

作　　者：颜小兵[1] 陈兴国[1] 秦金贵[1] INOKUCHI Makoto 

机构地区：[1]有机高分子光电功能材料(湖北省)重点实验室 武汉大学化学与分子科学学院,武汉430072 [2]Department of Materials Science and Engineering, Science University of Tokyo in Yamaguchi, Onoda, Yamaguchi 756-0884, Japan

出　　处：《无机化学学报》2010年第12期2237-2242,共6页Chinese Journal of Inorganic Chemistry

基　　金：国家自然科学基金资助项目(No.20774071)

摘　　要：将过渡金属配合物阳离子([M(DETA)2]n+(M=Cu2+,Ni2+,Co3+;DETA=Diethylenetriamine,二乙烯三胺)作为客体插入层状MnPS3层间得到了相应的3个夹层化合物。通过X-射线粉末衍射、元素分析和红外光谱对夹层化合物的结构进行了表征。结果表明,与主体MnPS3 0.65 nm的层间距相比较,夹层化合物(Mn0.88PS3[Cu(DETA)2]0.12)的层间距扩大了0.32 nm,由此推测客体[Cu(DETA)2]2+在层间以平面四方的配位形式存在,而另2个夹层化合物(Mn0.79PS3[Ni(DETA)2]0.21和Mn0.74PS3[Co(DETA)2]0.17)的层间距扩大了0.48nm,说明客体[(M(DETA)2]n+,M=Co3+,Ni2+)在主体层间以八面体配位形式存在。磁性测试结果表明过渡金属离子[(M(DETA)2]n+(M=Cu2+,Co3+)的插入能引起主体MnPS3的磁性在35～40 K发生由顺磁向亚铁磁性的转变并表现自发磁化,而客体[Ni(DETA)2]2+却使夹层化合物的反铁磁相互作用增强,抑制了自发磁化的发生。Three intercalation compounds based on the insertion of cationic complex guests（[M（DETA）2]n＋（M=Cu2＋,Ni2＋,Co3＋;DETA=Diethylenetriamine） into layered MnPS3 have been synthesized and characterized with X-ray powder diffraction,elemental analysis and infrared spectroscopy.Compared with pristine MnPS3 the lattice spacing of Mn0.88PS3[Cu（DETA）2]0.12 is expanded by about 0.32 nm suggesting that cationic [Cu（DETA）2]2＋ guest exists in square geometry at the interlayer space of MnPS3.But 0.48 nm of the lattice expansion for Mn0.79PS3[Ni（DETA）2]0.21 and Mn0.74PS3[Co（DETA）2]0.17 indicates that [M（DETA）2]n＋（M=Co3＋,Ni2＋） adopts the octahedral geometry.The magnetic measurements indicate that the intercalation of [M（DETA）2]n＋（M=Cu2＋,Co3＋） can induce the magnetic phase transition of MnPS3 slab from paramagnetism to ferrimagnetism at low temperature,but the insertion of [Ni（DETA）2]2＋ strengthens antiferromagntic interaction of the spins that suppresses the occurrence of spontaneous magnetization.

关 键 词：夹层作用 层状MnPS3 二乙烯三胺 配合物 磁性 

分 类 号：O614[理学—无机化学]