PTFE乳液制备PTFE/YSZ微孔膜及孔隙率的研究  

Preparation of PTFE/YSZ Composite Microporous Membrane by PTFE Resin Emulsion and Investigation on Porosity

作　　者：杜金丽[1] 邓新华[1] 孙元[1] 罗衍慧[1] 庞向川[1] 

机构地区：[1]天津工业大学材料科学与工程学院,天津300160

出　　处：《中国塑料》2010年第12期84-88,共5页China Plastics

摘　　要：以聚四氟乙烯(PTFE)乳液为原料、氧化钇稳定二氧化锆(YSZ)微纳米粉体为增强体,采用机械拉伸法制备了PTFE/YSZ复合微孔膜,通过扫描电子显微镜对其进行了表征,并运用单因素法探讨了分散剂聚乙烯醇(PVA)、拉伸倍数、YSZ含量和热处理温度对复合微孔膜孔隙率的影响。结果表明,在复合微孔膜中添加PVA以及增加YSZ含量均使复合微孔膜的孔隙率增大;在拉伸3.5倍、YSZ含量为8%(质量分数,下同)、热处理温度为320℃时,复合微孔膜孔隙率高达73.09%。In this paper, PTFE/YSZ composite microporous membrane was prepared by mechanical tension of a PTFE emulsion containing YSZ micro/nanoparticles. The structure and performance of PTFE/YSZ composite microporous membrane were characterized uisng scanning electron microscope （SEM）. The effects of the dispersant PVA, draw ratio, YSZ content, and calcination temperature on the porosity of composite microporous membrane were systematically investigated. It was found that the porosity increased significantly with increasing PVA and YSZ contents. The porosity reached 73. 09 % when the draw ratio was 3. 5 times, YSZ contents 8 %, and the calcinations temperature 320 ℃.

关 键 词：聚四氟乙烯 氧化钇稳定二氧化锆 微孔膜 孔隙率 

分 类 号：TQ320.721[化学工程—合成树脂塑料工业]