Stress Corrosion Cracking of Nitrogen-containing Stainless Steel 316LN in High Temperature Water Environments  

作　　者：YANG Wu LI Guangfu HUANG Chunbo ZHOU Jianjiang LU Zhanpeng 

机构地区：[1]Shanghai Research Institute of Materials, Shanghai 200437, China [2]Shanghai Key Laboratory for Engineering Materials Evaluation, Shanghai 20043 7, China

出　　处：《Chinese Journal of Mechanical Engineering》2010年第6期677-683,共7页中国机械工程学报（英文版）

基　　金：supported by National Basic Research Program of China (973 Program, Grant No. 2006CB605005);Shanghai Municipal Committee of Science and Technology of china(Grant No. 005207019,Grant No. 08520708000)

摘　　要：Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.

关 键 词：nitrogen-containing stainless steel stress corrosion cracking （SCC） potential SENSITIZATION slow strain rate test （SSRT） 

分 类 号：TG172.9[金属学及工艺—金属表面处理] TG142.71[金属学及工艺—金属学]