热处理态钢结硬质合金WC相析出微结构分析  

Microstructure Analysis on Precipitation of WC Phase in Heat Treated Steel-bonded Carbide

作　　者：赵一生[1,2] 魏世忠[3] 高志国[2] 

机构地区：[1]深圳职业技术学院 [2]中南大学 [3]河南科技大学

出　　处：《工具技术》2011年第1期31-33,共3页Tool Engineering

摘　　要：利用SEM研究了热处理后钢结硬质合金TLMW50复式碳化物中WC相的析出及其微结构。结果表明:经过1100℃淬火后烧结态钢结硬质合金TLMW50中主要复式碳化物Fe3W3C、Fe2W2C相发生析出分解,三角状、菱形状WC相颗粒随机分布在Fe3W3C、Fe2W2C相颗粒上。淬火二次析出WC相颗粒有利于提高烧结态钢结硬质合金TLMW50试样的硬度、耐磨性。XRD衍射分析结果表明;在回火温度150℃-250℃范围内,随着回火温度的升高,WC析出物数量明显减少。Precipitation and microstructure of WC phase from multiple carbides in heat treated Steel-bonded carbide TLMW50 were investigated by SEM. The results showed that the precipitation of WC phase from Fe3W3C,Fe2W2C phase was observed in TLMW50 as-quenched in 1100℃, the triangular or rhombie WC phase precipitates were randomly distributed in Fe3W3C,F2W2C phase particles. The precipitation of WC phase was propitious to increase the rigidity of the Steel-bonded carbide TLWM50. The XRD diffracting results showed that The numbers of WC phase precipitates decreased with the increasing of temper temperature from 150℃- 250℃.

关 键 词：热处理 钢结硬质合金 WC相 析出 微结构 

分 类 号：TG135[一般工业技术—材料科学与工程] TG161[金属学及工艺—合金]