冷轧Cu_(88)Fe_(12)合金的显微组织及性能  

Microstructure and properties of cold rolled Cu_(88)Fe_(12) alloys

作　　者：周志明[1] 曹敏敏[1] 唐丽文[1] 刘春[1] 王亚平[2] 

机构地区：[1]重庆理工大学材料科学与工程学院,重庆400054 [2]西安交通大学理学院,陕西西安710049

出　　处：《锻压技术》2010年第6期109-111,共3页Forging & Stamping Technology

基　　金：重庆市自然科学基金;重庆市教育委员会科学技术研究项目;新世纪优秀人才支持计划(NCET-07-0679);重庆理工大学基金(09-60-16)

摘　　要：通过室温下低应变速率大变形冷轧Cu88Fe12合金,研究了其显微组织和性能的变化。研究结果表明,经过冷轧变形后Cu88Fe12合金富Fe相的显微组织呈现出明显的纤维状,显微硬度刚开始变形时上升很快,随着变形的增加,增加的幅度逐步降低;电导率随着轧制变形的增加而降低,当达到一定量的大变形后,电导率又有所上升。The microstructures and properties of heavily cold rolled Cu88Fe12 alloys at low strain rate were studied at room temperature.The experiment results show that the microstructure of Fe-rich phases are deformed to ribbons filaments,the microhardness increases continuously with the increasing of rolling strain,the electrical conductivity first decreases gradually with the deformation strain,however,after deforming to certain degree,the electrical conductivity increases again.

关 键 词：Cu88Fe12合金 冷轧 显微组织 