NiAl-31Cr-3Mo合金高温氧化性能研究  

Oxidation Properties of NiAl-31Cr-3Mo Alloy at High Temperature

作　　者：张光业[1] 王金林[1] 张华 唐果宁[1] 

机构地区：[1]湖南科技大学机械设备健康维护重点实验室,湖南湘潭411201

出　　处：《稀有金属》2011年第1期12-16,共5页Chinese Journal of Rare Metals

基　　金：国防基础科研项目(A3720060115);湖南省科技厅项目(2008TP4024-2)资助

摘　　要：研究了NiAl-31Cr-3Mo合金在1250～1500K空气中的氧化行为。实验结果表明:在实验温度范围内,合金的氧化动力学曲线符合抛物线规律;氧化过程中合金表面生成了以α-Al2O3为主的氧化膜,并且含有Cr2O3。采用扫描电镜和能谱分析研究了氧化产物的微观组织及构成,并从合金的相组成探讨了NiAl-31Cr-3Mo合金的氧化机制。The isothermal oxidation behavior of NiAl-31Cr-3Mo alloy at 1250～1500 K in static air atmosphere was investigated.The experimental results revealed that the isothermal oxidation kinetics of the tested alloy agreed with the parabolic law at all test temperatures.The oxidation layer consisted of α-Al2O3 and little Cr2O3 on the surface of the tested alloy.The microstructure and composite of the oxide layer were studied by X-ray diffractometer,scanning electron microscope with an EDAX unit.The oxidation mechanism was discussed from the phase constitute for NiAl-31Cr-3Mo alloy.

关 键 词：金属间化合物 NIAL基合金 微观组织 氧化性能 

分 类 号：TG174.45[金属学及工艺—金属表面处理]